Characterization of Electrochemically Activated Surface on Rolled Commercial AA8006 Alumnium

  • Yingda Yu (a1), Øystein Sævik (a1), Jan Halvor Nordlien (a2) and Kemal Nisancioglu (a1)

Abstract

Commercial alloy AA8006 (nominal composition in wt%1.5Fe, 0.4Mn, 0.2Si) exhibits electrochemical activation in chloride media as a result of annealing at temperatures above 350°C. Activation is manifested by a significant negative shift in the corrosion potential and a significant increase in the anodic current when polarized above the corrosion potential in aqueous chloride solution. This phenomenon was correlated with the enrichment of trace element Pb at the oxide-metal interface. For fixed annealing time, maximum activation and Pb-enrichment are obtained at an annealing temperature of 450 °C independent of the original surface condition. Reduced activation with increasing temperature is attributed to increasing density of the spinel crystalline phase to cause the passivity of the surface.

Copyright

References

Hide All
1. Leth-Olsen, H., Nordlien, J. H., and Nisancioglu, K., J. Electrochem. Soc., 144, L196 (1997).
2. Leth-Olsen, H. and Nisancioglu, K., Corros. Sci., 40, 1179 (1998).
3. Leth-Olsen, H., Afseth, A. and Nisancioglu, K., Corros. Sci., 40, 1195 (1998).
4. Leth-Olsen, H., Nordlien, J. H., and Nisancioglu, K., Corros. Sci., 40, 2051 (1998).
5. Keuong, Y. W., Nordlien, J. H. and Nisancioglu, K., J. Electrochem. Soc., 148, B497 (2001).
6. Afseth, A., Nordlien, J. H., Scamans, G. M., and Nisancioglu, K., Corros. Sci., 43, 2259 (2002).
7. Afseth, A., Nordlien, J. H., Scamans, G. M., and Nisancioglu, K., Corros. Sci., 44, 145 (2002).
8. Keuong, Y. W., Ono, S., Nordlien, J. H. and Nisancioglu, K., J. Electrochem. Soc., 150, B547 (2003).
9. Gundersen, J. T. B., Aytac, A., Nordlien, J. H. and Nisancioglu, K., Corros. Sci., 46, 265 (2004).
10. Nisancioglu, K. and Holtan, H., Corros. Sci., 18, 835 (1978).
11. Gundersen, J. T. B., Aytac, A., Nordlien, J. H. and Nisancioglu, K., Corros. Sci., 46, 679 (2004).
12. Sævik, Ø., Yu, Y., Nordlien, J. H. and Nisancioglu, K., submitted to J. Electrochem. Soc. (2004).
13. Tsubakino, H., Nogami, A., Yamamoto, A., Terasawa, M, Mitamura, T, Yamanoi, T., Kinomura, A. and Horino, Y., Materials Sci. Form, 396–402, 435 (2002).
14. Furneaux, R., Thompson, G.E. and Wood, G.C., Corros. Sci., 18, 853 (1978).
15. Field, D.J., Scamans, G. M. and Butler, E.P., Metall. Tran. 18A, 463 (1987).
16. Lea, C. and Seah, M.P., Philos. Mag., 35, 213 (1977).

Related content

Powered by UNSILO

Characterization of Electrochemically Activated Surface on Rolled Commercial AA8006 Alumnium

  • Yingda Yu (a1), Øystein Sævik (a1), Jan Halvor Nordlien (a2) and Kemal Nisancioglu (a1)

Metrics

Full text views

Total number of HTML views: 0
Total number of PDF views: 0 *
Loading metrics...

Abstract views

Total abstract views: 0 *
Loading metrics...

* Views captured on Cambridge Core between <date>. This data will be updated every 24 hours.

Usage data cannot currently be displayed.