Characterization of Electrically Pulsed Chromium Disilicide Fusible Links

Published online by Cambridge University Press:  10 February 2011

A.G. Domenicucci ,
B. Cunningham  and
P. Tsang
A.G. Domenicucci
Affiliation:
IBM Microelectronics Division, 1580 Route 52, Hopewell Junction, New York 12533
B. Cunningham
Affiliation:
Dominion Semiconductor, 9600 Goodwin Drive, Manassas, Virginia 20110
P. Tsang
Affiliation:
Micrus Coporation 1580 Route 52, Hopewell Junction, New York 12533
Get access

Abstract

Fusible links, fabricated from silicon rich chromium disilicide thin films, were subjected to voltage pulses in the 3–6 volt range. An optimum voltage existed at which the fuses blew. Transmission electron microscopy (TEM) was used to study the microstructural characteristics of the fuses both before and after the application of the voltage pulses. The TEM characterization, coupled with electrical and physical measurements, revealed that the mechanism underlying the fuse blow was hole current induced Si electromigration. Below the optimum voltage, the amount of Si transported was insufficient to cause fuse rupture. Above the optimum voltage, the current- voltage characteristics of the fuses became nonlinear and a unique sequence of material phases was formed. The composition of the phases suggests that both thermomigration and electromigration processes were operating at voltages above the optimum voltage.

Type
Research Article
Information
MRS Online Proceedings Library (OPL) , Volume 523: Symposium U – Electron Microscopy of Semiconducting Materials & ULSI Devices , 1998 , 103
Copyright
Copyright © Materials Research Society 1998

Access options

Get access to the full version of this content by using one of the access options below. (Log in options will check for institutional or personal access. Content may require purchase if you do not have access.)

References

1. Smith, R.J., IEEE IEDM 82, Techn Digest, p 608(1982).Google Scholar
2. Schuster, S.E., IEEE J. Solid State Circuits, SC-13, p698(1978).10.1109/JSSC.1978.1051122Google Scholar
3. Shinoda, D., Asanabe, S., and Sasaki, Y., J. Phys. Soc. Jap. 19, p 269 (1964).10.1143/JPSJ.19.269Google Scholar
4. Waits, R.K., J. Vac. Sci. Tech. 6, p 308 (1968).10.1116/1.1492682Google Scholar
5. Nashida, J., J. Mat. Sci. 7, p 1119 (1972).10.1007/BF00550193Google Scholar
6. Heiber, K. and Dittmann, R., Thin Solid Films 36, p 357 (1976).10.1016/0040-6090(76)90033-XGoogle Scholar
7. Nashida, I. and Sakata, T., J. Phys. Chem. Solids 39, p 499 (1978).Google Scholar
8. Bedeker, C.J., Kritzinger, S., and Lombaard, J.C., Thin Solid Films 141, p 117 (1986).10.1016/0040-6090(86)90325-1Google Scholar
9. Domenicucci, A., Fitzgibbon, G., Tsang, P., Kastl, R., to be published.Google Scholar
10. Benedict, J., Anderson, R., and Klepeis, S.J. in Specimen Preparation for Transmission Electron Microscopy of Materials III, ed. by Anderson, R., Tracy, B., and Bravman, J.(Mat. Res. Soc. Symp. Proc. 254, Pittsburg, PA 1992), pp. 121–140.Google Scholar
11. Cunningham, B., private communication.Google Scholar
12. Sze, S.M., Physics of Semiconductor Devices, Wiley-Interscience, New York, 1981, p21.Google Scholar