  • R. D. James (a1), D. L. Paisley (a2), K. A. Gruss (a1), S. Parthasarthi (a3), B. R. Tittmann (a3), Y. Horie (a4) and R. F. Davis (a1)...

Abstract

To assess the adhesion of nitride coatings on metals, titanium 6% aluminum 4% vanadium substrates were coated with titanium nitride (TiN) using both cathodic arc and electron beam evaporation. Titanium aluminum nitride ((Ti, Al)N) was also deposited using cathodic arc evaporation. The interfaces of the coated samples were loaded in tension using a high speed shock wave which caused spallation either at the interface, in the coating or in the metal. Scanning acoustic microscopy analysis of the spalled samples detected delaminations at the interface in the samples deposited by cathodic arc evaporation. DYNA2D modeling of plate impact spallation experiments revealed the tensile adhesion strength for TiN deposited by both techniques was ≈ 2.0 GPa. The tensile adhesion strength for (Ti, Al)N was less than 1.5 GPa.

Copyright

References

Hide All
1. Burnett, P. J. and Rickerby, D. S., J. Mat. Sci. 23, 2429 (1988).
2. Coll, B. F., Sathrum, P., Fontana, R., Peyre, J. P., Duchateau, D. and Benmalek, M., Surf. Coat. Technol. 52, 57 (1992).
3. Parameswaran, V. R., Surf. Coat. Technol. 52, 251 (1992).
4. Mitall, K. L., Ed., ASTM STP 640 Adhesion Measurements of Thin Films, Thick Films, and Bulk Coatings (ASTM, Philadelphia, PA, 1978).
5. Perry, A. J., Thin Solid Films 81, 357 (1981).
6. Bull, J. S. and Rickerby, D. S., in Surface Modifications Technologies III, Sudarshan, T. S. and Bhat, D. G., Eds. (The Minerals, Metals & Materials Society, 1990) p. 153.
7. Gupta, V., Argon, A. S., Cornie, J. A. and Parks, D. M., Mat. Sci. Eng A126, 105 (1990).
8. Gupta, V., Yuan, J. and Pronin, A., J. Adhesion Sci. Technol. 8, 713 (1994).
9. Nutt, G. L., Lai, W., Froeschner, K. E. and King, W. E., in Metal-Ceramic Interfaces, Ruhle, M., Evans, A. G., Ashby, M. F. and Hirth, J. P., Eds. (Acta-Scripta Metallurgica, 1989) p. 307.
10. Nutt, G. L. and King, W. E., Mat. Sci. Eng A159, 135 (1992).
11. Snowden, W. E. and Asay, I. A., Mater. Sci. Res 14, 651 (1981).
12. Vossen, J. L., in ASTM STP 640 Adhesion Measurements of Thin Films, Thick Films, and Bulk Coatings, Mitall, K. L., Ed. (ASTM, Philadelphia, PA, 1978) p. 122.
13. Yuan, J., Gupta, V., J. Appl. Phys. 74, 2388 (1993).
14. Hemsing, W. F., Rev. Sci. Instrum. 50, 73 (1979).
15. Warnes, R. H., Paisley, D. L. and Tonks, D. L., presented at The American Physical Society Conference on Shock Compression of Condensed Matter, Seattle, WA, August 13–18 1995. (unpublished).
16. Sathrum, P. and Coll, B. F., Surf. Coat. Technol. 50, 103 (1992).
17. Halloquist, J. O., UCID-18756, Rev. 3 (Lawrence Livermore National Laboratory, 1987)
18. Steinberg, D. J., UCRL-MA-106439 (Lawrence Livermore National Laboratory, 1991)
19. Briggs, A., Acoustic Microscopy (Oxford University Press, New York, 1992)

Adhesion Evaluation of TiN and (Ti, Al)N Coatings on Titanium 6Al-4V

  • R. D. James (a1), D. L. Paisley (a2), K. A. Gruss (a1), S. Parthasarthi (a3), B. R. Tittmann (a3), Y. Horie (a4) and R. F. Davis (a1)...

Metrics

Full text views

Total number of HTML views: 0
Total number of PDF views: 0 *
Loading metrics...

Abstract views

Total abstract views: 0 *
Loading metrics...

* Views captured on Cambridge Core between <date>. This data will be updated every 24 hours.

Usage data cannot currently be displayed