Activation Volume for Inelastic Deformation in Polycrystalline Ag Films at Low Temperatures

Published online by Cambridge University Press:  10 February 2011

Mauro J. Kobrinsky
Affiliation:
kobrinsm@mit.edu
Carl V. Thompson
Affiliation:
Materials Science and Eng. Dept., Massachusetts Institute of Technology, 77 Massachusetts Ave., Cambridge, MA, USA 02139.
Get access

Abstract

The low temperature (T < 100 °C) inelasticity of polycrystalline Ag thin films on thick substrates has been studied. In-situ Transmission Electron Microscopy and stress-relaxation experiments indicate that thermally-activated glide of dislocations through forest-dislocation obstacles is the dominant inelastic mechanism. Values of the activation volume for inelastic deformation obtained with both experiments are reported. The mean distance between obstacles along the length of moving dislocations was found to be significantly smaller than the thickness of the film and the average grain size, which explains why current models for dislocationmediated plasticity underestimate the strength of thin films. Results from these experiments on Ag are expected to be representative of other metallic thin films (e.g. Cu and Au) on substrates.

Type
Research Article
Copyright
Copyright © Materials Research Society 2000

Access options

Get access to the full version of this content by using one of the access options below. (Log in options will check for institutional or personal access. Content may require purchase if you do not have access.)

References

REFERENCES

1. Kobrinsky, M. J. and Thompson, C. V., Appl. Phys. Lett. 73, 2429 (1998).Google Scholar
2. Nix, W. D., Metall. Trans. 20A, 2217 (1989).Google Scholar
3. Kuan, T. S. and Murakami, M., Metall. Trans. 13A, 383 (1982).Google Scholar
4. Venkatraman, R. and Bravman, J. C., J. Mater. Res. 7, 2040 (1992).Google Scholar
5. Freund, L. B., J. Appl. Mech. 54, 553 (1987).Google Scholar
6. Thompson, C. V., J. Mater. Res. 8, 237 (1993).Google Scholar
7. Nix, W. D., Scripta Mat. 39, 545 (1998).Google Scholar
8. Kobrinsky, M.J. and Thompson, C.V., accepted for publication in Acta Materialia, Aug. 1999.Google Scholar
9. Blanchet, A., Masters Thesis, Massachusetts Institute of Technology, Cambridge, MA (1998).Google Scholar
10. Carel, R., Ph. D.dissertation, Massachusetts Institute of Technology, Cambridge, MA (1995).Google Scholar
11. Thompson, C. V. and Carel, R., J. Mech. Phys. Solids 44, 657 (1996).Google Scholar
12. Thompson, C. V., Annu. Rev. Mater. Sci. 20, 245 (1990).Google Scholar
13. Simmons, G., Wang, W., Single crystal elastic constants and calculated aggregate properties: a handbook, 2nd ed., (M.I.T. Press, Cambridge, 1971).Google Scholar
14. Kocks, U. F., Argon, A. S. and Ashby, M. F., Thermodynamics and Kinetics of Slip, Prog. Mater. Sci., eds. Chalmers, B., Christian, J. W., and Massalski, J. B., 19, 26 (1975).Google Scholar
15. Argon, A. S., Mechanical Properties of Single-Phase Crystalline Media: Deformation at Low Temperatures, 4th edition, eds. Cahn, R. W. and Haasen, P., (North-Holland, 1996) pp. 878.Google Scholar
16. Argon, A. S. and East, G. H., in Proceedings of the 5th International Conference on the Strength of Metals and Alloys, eds. Haasen, P., Gerold, V., and Kostorz, G., 1, 9 (1979).Google Scholar
17. Tanoue, K., Acta metall. mater. 40, 1945 (1992).Google Scholar
18. Friedel, J., ”Dislocations” (Addison-Wesley Pub. Co, New York, 1967).Google Scholar
19. Conrad, H. and Cao, W. D., in Proceedings of the Johannes Weertman Symposium, (The Minerals, Metals & Materials Society, 1996) pp. 321.Google Scholar
20. Prasad, Y. V. R. K., Sastry, D. H., Vasu, K. I., Journal of Materials Science 5,495 (1970).Google Scholar
21. Kassner, M. E. and Mukherjee, A. K., Scripta metall. 17, 741 (1983).Google Scholar