Leaching Behavior of Simulated Radioactive Waste Glass by Neutron Activation Method

Published online by Cambridge University Press:  25 February 2011

Seichi Sato
Affiliation:
Department of Nuclear Engineering, Faculty of Engineering, Kyushu University, Hakozaki Higashi-ku, Fukuoka 812, JAPAN
Hirotaka Furuya
Affiliation:
Department of Nuclear Engineering, Faculty of Engineering, Kyushu University, Hakozaki Higashi-ku, Fukuoka 812, JAPAN
Kazuaki Ohta
Affiliation:
Department of Nuclear Engineering, Faculty of Engineering, Kyushu University, Hakozaki Higashi-ku, Fukuoka 812, JAPAN
Masayasu Sugisaki
Affiliation:
Department of Nuclear Engineering, Faculty of Engineering, Kyushu University, Hakozaki Higashi-ku, Fukuoka 812, JAPAN
Tadaharu Tanai
Affiliation:
Research Reactor Institute, Kyoto University, Kumatori-cho Sennan-gun, Osaka 590-04, JAPAN
Get access

Abstract

Simulated radioactive waste glass was irradiated in a nuclear reactor and radiation damage was induced by 10B(n,0)7Li reaction up to 0.14 displacement per atom. Static leach tests of the activated waste glass were carried out at 40°C, up to 38 days. Concentration of elements in leachate was determined by gamma-spectrometry. The leach test of non-irradiated glass was also performed at 40°C up to 82 days in which the solution concentration of elements was determined by an atomic absorption analysis. Leach results are given in terms of normalized elemental mass loss for the seven elements Na, K, Cs, Ca, Zn, La and Ce. Normalized elemental mass loss of alkali ions was proportional to square root of time and then, was proportional to time. Normalized elemental mass loss of alkali earth ions did not show such a simple tendency. Build up of zinc on the waste glass surface was observed following its initial leaching. It was also found that theleach rate of Cs, Zn and Ce decreased with increase of irradiation exposure of waste glass.

Type
Research Article
Copyright
Copyright © Materials Research Society 1984

Access options

Get access to the full version of this content by using one of the access options below. (Log in options will check for institutional or personal access. Content may require purchase if you do not have access.)

References

REFERENCES

1. Mendel, J.E., Nelson, R.D., Turcotte, R.P., Gray, W.J., Merz, M.D., Roberts, F.P., Weber, W.J., Westrik, J.H. Jr. and Clark, D.E., PNL 3802 (1981).Google Scholar
2. Weber, W.J. and Roberts, F.P., Nucl. Technol. 60, 178 (1983).10.13182/NT83-A33073Google Scholar
3. MCC-l Static Leach Test (1982) Materials Characterization Center, Battelle Pacific Northwest Laboratory Richland, Washington.Google Scholar
4. Manning, I and Mueller, G.P., Comp. Phys. Comm. 7, 85 (1974).10.1016/0010-4655(74)90043-5Google Scholar
5. Mendel, J.E., Ross, W.A., Roberts, F.P., Turcotte, R.P., Katayama, Y.B. and Westsik, J.H. Jr., (1976) in “Management of Radioactive Waste from the Nuclear Fuel Cycle”, Vol. 2, IAEA, pp.49.Google Scholar
6. Kiso, Y. and Tamai, T., Genshiryoku-Kogyo 17(11), 38 (1971).Google Scholar
7. Bates, J.K., Jardine, L.J., Flynn, K.F. and Steinder, M.J., ANL-81-34 (1982).Google Scholar
8. Malow, G. and Schiewer, E., HMI-B217 (1977).Google Scholar
9. Hench, L.L., Clark, D.E., Lue Yen-Bower, E., Nucl. Chem. Waste Manage. 1, 59 (1980).10.1016/0191-815X(80)90029-7CrossRefGoogle Scholar
10. Diamond, H. and Friedman, A.M., Nucl. Chem. Waste Manage. 2, 207 (1981).10.1016/0191-815X(81)90017-6Google Scholar
11. Burns, W.G., Hughes, A.E., Marples, J.A.C., Nelson, R.S. and Stonneham, A.M., J. Nucl. Mater. 107, 245 (1982).10.1016/0022-3115(82)90424-XGoogle Scholar