Electron-beam additive manufacturing of high-temperature metals

Published online by Cambridge University Press:  10 October 2016

Lawrence E. Murr  and
Shujun Li
Lawrence E. Murr
Affiliation:
Department of Metallurgical, Materials and Biomedical Engineering, The University of Texas at El Paso, USA; lemurr@utep.edu
Shujun Li
Affiliation:
Institute of Metal Research, Chinese Academy of Sciences, China; shjli@imr.ac.cn
Get access

Abstract

This article overviews electron-beam melting (EBM), including process optimization issues. Examples of EBM-fabricated components described include hexagonal close-packed Ti-6Al-4V, face-centered-cubic René 142 (a Ni-based superalloy), and body-centered-cubic pure iron, corresponding to a melt temperature range from 1375°C to 1630°C. Residual microstructures observed for these fabricated components by optical microscopy, scanning electron microscopy, and transmission electron microscopy include equilibrium as well as nonequilibrium features, which illustrate prospects for novel structure–property manipulation in the EBM process. The EBM process relies on available pre-alloyed, precursor powders that are selectively melted layer by layer by a computer-aided design scanned electron beam to form relatively small, but often complex, products or components. Direct metal deposition innovations capable of truly three-dimensional metal printing are described, especially high-temperature metals and alloys for future additive manufacturing technologies.

Keywords

electron-beam meltinghigh-temperature metalsmicrostructures
Type
Research Article
Information
MRS Bulletin , Volume 41 , Issue 10: Metallic materials for 3D printing , October 2016 , pp. 752 - 757
Copyright
Copyright © Materials Research Society 2016 

Access options

Get access to the full version of this content by using one of the access options below. (Log in options will check for institutional or personal access. Content may require purchase if you do not have access.)

References

Bontha, S., Klingbeil, N.W., Kobryn, P.A., Mater. Sci. Eng. A 513–514, 311 (2009).Google Scholar
Gaytan, S.M., Murr, L.E., Medina, F., Martinez, E., Lopez, M.I., Wicker, R.B., Mater. Technol. 24 (3), 180 (2009).CrossRefGoogle Scholar
Gong, X., Anderson, T., Chan, K., Manuf. Rev. 1, 2 (2014).Google Scholar
Smith, C.J., Derguti, F., Hernandez Nava, E., Thomas, M., Tammas-Williams, S., Gulizia, S., Fraser, D., Todd, I., J. Mater. Process. Technol. 229, 128 (2015).Google Scholar
Korner, C., Int. Mater. Rev. 61 (5), 361 (2016).Google Scholar
Murr, L.E., Gaytan, S.M., Medina, F., Lopez, H., Martinez, E., Machado, B.I., Philos. Trans. R. Soc. Lond. A 368, 1999 (2010).Google Scholar
Murr, L.E., Amato, K.N., Li, S.J., Tian, Y.X., Cheng, X.Y., Gaytan, S.M., J. Mech. Behav. Biomed. Mater. 4, 1396 (2011).CrossRefGoogle Scholar
Oblak, J.M., Kear, B.H., in Electron Microscopy and Structure of Materials, Thomas, G., Fulrath, R.M., Fisher, R.M., Eds. (University of California Press, Berkeley, 1972), p. 566.Google Scholar
Murr, L.E., Martinez, E., Pan, X.M., Gaytan, S.M., Castro, J.A., Terrazas, C.A., Medina, F., Wicker, R.B., Abbott, D.H., Acta Mater. 61 (1), 4289 (2013).Google Scholar
Murr, L.E., Martinez, E., Pan, X.M., Meng, C.M., Yang, J., Li, S.J., Yang, F., Xu, Q., Hernandez, J., Zhu, W.J., Gaytan, S.M., Medina, F., Wicker, R.B., J. Mater. Res. Technol. 2 (4), 376 (2013).CrossRefGoogle Scholar
Orme, M., J. Mater. Eng. Perform. 2 (3), 399 (1993).Google Scholar
Orme, M., Smith, R.F., J. Manuf. Sci. Eng. 22 (3), 484 (2000).CrossRefGoogle Scholar
Tseng, A.A., Lee, M.H., Zhao, B., J. Eng. Mater. Technol. 123 (1), 74 (2001).CrossRefGoogle Scholar
Michaelis, B.U., Dunn-Rankin, D., Smith, R.F., Bobrow, J.E., Int. J. Heat Mass Trans. 50, 4554 (2007).CrossRefGoogle Scholar
Chao, Y.-P., Qi, L.-H., Xiao, Y., Luo, J., Zhou, J.-M., J. Mater. Process. Technol. 212 (2), 484 (2012).CrossRefGoogle Scholar