Effects on the amorphous Ga2O3 film surfaces by sub-IB-metal-nano-layers

  • L. I. Juárez-Amador (a1), M. Galván-Arellano (a2), Y. M. Hernández-Rodríguez (a1), J. A. Andraca-Adame (a3), G. Romero-Paredes (a2) and R. Peña-Sierra (a2)...

Abstract

This work reports by the first time a method to control the geometry of Ga2O3 films nanocrystallites at 350 °C. The formation of controlled shaped nano-crystallites of γ-Ga2O3 from amorphous Ga2O3 films grown by RF-Sputtering at room temperature driven by nano-layers of group IB metals (Cu, Ag or Au) is studied. The reported results can be explained by the role of subsurface metal nano-layers and the non-equilibrium nature of the sputtering processes. To study the effects on the surface structure and their optical properties arrays of amorphous-Ga2O3/IB-metal/amorphous-Ga2O3 were annealed in dry N2 atmosphere at 350 °C by 50, 100 and 150 min. The experimental results can be explained by the evolution of the amorphous character of the films amorphous films towards the nanocrystalline γ-Ga2O3 phase driven by the metal nano-layer seed nature. As the annealing time was increased the transition from amorphous-Ga2O3 to the nanocrystalline γ-Ga2O3 phase was detected by X-ray diffraction analysis. The transition to the nanocrystalline γ-Ga2O3 is demonstrated by the formation of octahedral, triangle and ball shape nanocrystallites with sizes of ∼5 to 50 nm according to FE-SEM analysis. The influence of the metal nano-layer is clearly seen by the shift of the plasmon frequency resonance produced by the Ga2O3/IB-metal/Ga2O3 arrays in the region from 400 to 600 nm caused by the modification of the interface Ga2O3/IB-metal produced by the applied annealing stages.

Copyright

Corresponding author

References

Hide All
[1]Alves, E. et al., Nucl. Instruments Methods Phys. Res. Sect. B Beam Interact. with Mater. Atoms 272, 6165 (2012).
[2]Won, Y. H. and Stanciu, L. A., Sensors (Switzerland), 12 (10), 1301913033 (2012).
[3]Wang, X. B., Song, C., Geng, K. W., Zeng, F., and Pan, F., J. Phys. D. Appl. Phys. 39 (23), 49924996 (2006).
[4]Das, S. and Alford, T. L., J. Appl. Phys. 113 (24), 17 (2013).
[5]Gong, H., Hu, J. Q., Wang, J. H., Ong, C. H., and Zhu, F. R., Sensors Actuators, B Chem. 115 (1), 247251 (2006).
[6]Hayashi, H., Huang, R., Oba, F., Hirayama, T., and Tanaka, I., J. Mater. Res. 26 (04), 578583 (2011).
[7]Eranna, G. et al., A Compr. Rev. Crit. Rev. Solid State Mater. Sci. 8436, 111118 (2010).
[8]Montes-Valenzuela, I., Romero-Paredes, G., Vázquez-Agustín, M. A., Baca-Arroyo, R., and Peña-Sierra, R., Mater. Sci. Semicond. Process 37, 185189 (2015).
[9]Cullity, B. D., Elements of X-Ray Diffraction, 2nd ed. (Addison-Wesly, Reading, Massachusetts, 1978).
[10]Truong, V. V. and Scott, G. D., J. Opt. Soc. Am. 67 (4), 502510 (1977).
[11]Bader, G., Ashrit, P. V., Girouard, F. E., and Van Truong, V., J. Appl. Phys. 68 (4), 18201824 (1990).
[12]Xu, G., Tazawa, M., Jin, P., and Nakao, S., Appl. Phys. A Mater. Sci. Process. 80 (7), 15351540 (2005).

Keywords

Metrics

Full text views

Total number of HTML views: 0
Total number of PDF views: 0 *
Loading metrics...

Abstract views

Total abstract views: 0 *
Loading metrics...

* Views captured on Cambridge Core between <date>. This data will be updated every 24 hours.

Usage data cannot currently be displayed