Crystallization Behavior and Recoilless Fraction Determination of Amorphous and Nanocrystalline Fe56Co24Nb4B13Si2Cu1 System

Published online by Cambridge University Press:  27 February 2017

Monica Sorescu ,
Julia Limongelli ,
Christopher Stroh  and
Kevin Byerly
Monica Sorescu*
Affiliation:
Duquesne University, Department of Physics, Fisher Hall, Pittsburgh, PA 15282
Julia Limongelli
Affiliation:
Duquesne University, Department of Physics, Fisher Hall, Pittsburgh, PA 15282
Christopher Stroh
Affiliation:
Duquesne University, Department of Physics, Fisher Hall, Pittsburgh, PA 15282
Kevin Byerly
Affiliation:
SPANG, Magnetic Technology Center, 110 Delta Drive, Pittsburgh, PA 15238
*
*(Email: sorescu@duq.edu)
Get access

Abstract

Amorphous ferromagnetic alloy with the composition Fe56Co24Nb4B13Si2Cu1 was obtained by rapid quenching from the melt. Samples cut from the ribbons were annealed at 450, 550, 650 and 750 °C in a vacuum furnace. 57Fe Mössbauer spectroscopy was used to identify the phases formed based on the refined values of the hyperfine parameters. The as-quenched specimen was analyzed with a hyperfine magnetic field distribution and corresponded to an in-plane orientation of the magnetic moment directions. The sample annealed at 450 °C was found to be in a nanocrystalline state due to observation of the (FeCo)-Si alloy with the DO3 structure. The balance of the composition was represented by a metalloid-enriched amorphous grain boundary phase. In contradistinction to this, the samples annealed at 550-750 °C were totally crystallized and the new phases formed were α-(FeCo), (FeCo)2(BSi) and (FeCo)3(BSi). These findings suggest that nanocrystallization is obtained only at select processing temperatures. A new set of Mössbauer spectra was obtained by recording simultaneously the intensity transmitted by a sandwich of the sample with the stainless steel etalon, based on the dual absorber method recently introduced by us. The values of the recoilless fraction can be derived from the relative spectral areas. The f factor value dropped from 0.6 to 0.37 for the sample annealed at 450 °C, consistent with the onset of nanocrystallization in the system. For the completely crystallized specimens, the f factor maintained values close to 0.5. This indicates that the presence of quenched-in stresses may play a role in the ability of samples to undergo recoilless emission and absorption of gamma rays.

Keywords

amorphousMössbauer effectnanoscale
Type
Articles
Information
MRS Advances , Volume 2 , Issue 27: Mechanical Behavior and Failure Mechanisms of Materials , 2017 , pp. 1435 - 1440
Copyright
Copyright © Materials Research Society 2017 

Access options

Get access to the full version of this content by using one of the access options below. (Log in options will check for institutional or personal access. Content may require purchase if you do not have access.)

References

REFERENCES

Duhaj, P., Matko, I., Svec, P., Sitek, J., Janickovic, D., Mater. Sci. Eng. B 39, 208 (1996).Google Scholar
Clavaguera, N., Pradell, T., Jie, Z., Clavaguera-Mora, M.T., Nanostruct. Mater. 6, 453 (1995).CrossRefGoogle Scholar
Lashgari, H.R., Chu, D., Xie, S., Sun, H., Ferry, M., Li, S., J. Non-Cryst. Solids 391, 4161 (2014).Google Scholar
Hoque, S.M., Hakim, M.A., Khan, F.A., Chau, N., Mater. Chem. Phys.101, 112 (2007).Google Scholar
Li, X.D., Yuan, W.Z., Zhao, Z.J., Wang, X.Z., Ruan, J.Z., Yang, X.L., J. Magn. Magn. Mater. 279, 429 (2004).CrossRefGoogle Scholar
Hakim, M.A., Hoque, S.M., J. Magn. Magn. Mater. 284, 395 (2004).CrossRefGoogle Scholar
Sorescu, M., Xu, T., Herchko, S., J. Magn. Magn. Mater. 323, 2859 (2011).Google Scholar
Gorria, P., Prida, V.M., Tejedor, M., Hernando, B., Sanchez, M.L., Phys. B 299, 215 (2001).Google Scholar
Duhaj, P., Svec, P., Sitek, J., Janickovic, D., Mater. Sci. Eng. A 304-306, 178 (2001).Google Scholar
Zhou, F., He, K.Y., Lu, K., Nanostruct. Mater. 9, 535 (1997).Google Scholar
Sorescu, M., Knobbe, E.T., Phys. Rev. B 52, 16086 (1995).Google Scholar
Sorescu, M., Knobbe, E.T., Barb, D., J. Phys. Chem. Solids 56, 79 (1995).Google Scholar
Sorescu, M., Mater. Lett. 54, 256 (2002).Google Scholar