Unusual SEM Image Contrast from Corrosion Oxide Films of Zr-2.5%Nb Pressure Tube Alloy

Published online by Cambridge University Press:  02 July 2020

Y. P. Lin  and
J. DeLuca
Y. P. Lin
Affiliation:
Materials Department, Ontario Hydro Technologies, Toronto, OntarioM8Z 5S4, Canada
J. DeLuca
Affiliation:
Materials Department, Ontario Hydro Technologies, Toronto, OntarioM8Z 5S4, Canada
Get access

Extract

Zr-2.5wt%Nb alloy is used as the pressure tube material in CANDU reactors. The pressure tube microstructure consists primarily of α-Zr (< l%Nb) grains elongated in the axial direction of the pressure tube and typically 0.3-0.5 μm thick in the radial direction. The α-Zr grains are partially surrounded by a thin layer of Nb-rich β-Zr phase (≈ 20%Nb). During corrosion, α-Zr is converted primarily to monoclinic ZrO2 with minor amounts of tetragonal ZrO2. Oxidation of α-Zr is complicated by the metastable nature of the phase below 863K. A detailed understanding of the nature of oxidized β-Zr remains a topic of on-going investigation, although some information have recently become available. Present SEM observations shed some lights on the charging characteristics of the oxidized β-Zr compared with ZrO2.

Oxide films on pre-polished surfaces perpendicular to the radial direction of the pressure tube were grown in steam at 673K in an autoclave; the treatment corresponds to the last stage of the pressure tube production.

Type
Oxidation, Corrosion, and Protective Coatings
Information
Microscopy and Microanalysis , Volume 3 , Issue S2: Proceedings: Microscopy & Microanalysis '97, Microscopy Society of America 55th Annual Meeting, Microbeam Analysis Society 31st Annual Meeting, Histochemical Society 48th Annual Meeting, Cleveland, Ohio, August 10-14, 1997 , August 1997 , pp. 781 - 782
Copyright
Copyright © Microscopy Society of America 1997

Access options

Get access to the full version of this content by using one of the access options below. (Log in options will check for institutional or personal access. Content may require purchase if you do not have access.)

References

Cheadle, B.A. and Aldridge, S.A, J. Nucl. Mater, 47(1973)255.10.1016/0022-3115(73)90109-8CrossRefGoogle Scholar
Lin, Y.P., Proc. 3rd Int. Conf. on Microscopy of Oxidation, U.K. Sept., 1996Google Scholar
Woo, O.T. and Lin, Y.P., submitted to J. Nucl. Mater.Google Scholar
Newbury, D.E.et al.Advanced Scanning Electron Microscopy and X-Ray Microanalysis, NewYork:Plenum Press (1986)45.10.1007/978-1-4757-9027-6_2CrossRefGoogle Scholar
This work was supported by funding from Ontario Hydro.Google Scholar