Surface analysis of a heat-treated, Al-containing, iron-based superalloy

  • M. F. López (a1), A. Gutiéerrez (a1), M. C. García-Alonso (a1) and M. L. Escudero (a1)

Abstract

The surface composition of MA 956 superalloy both as-received and after four exposure times at 1100 °C has been investigated by energy dispersive x-ray spectrometry (EDX) and x-ray photoelectron spectroscopy (XPS). The passive layer of the as-received sample is mainly formed by Cr- and Fe-oxides. Heat treatment leads to the formation of an alumina layer on which small nodules grow. XPS spectra evidence the presence of titanium and yttrium oxides at the surface of the heat-treated samples, suggesting Y and Ti outward diffusion through the alumina layer. Iron and chromium oxides at the topmost surface layers are observed only for short heat-treatment times.

Copyright

References

Hide All
1.Huntz, A. M., in Role of Active Elements in the Oxidation Behavior of High Temperature Metals and Alloys, edited by Lang, E. (Elsevier Applied Science, London, 1989), p. 81.
2.Bennett, M. J. and Houlton, M. R., in High Temperature Materials for Power Engineering, edited by Bachelet, F. (Kluwer Academic Publishers, Dordrecht, 1990), p. 189.
3.Benjamin, J. S., in New Materials by Mechanical Alloying Techniques, edited by Arzt, E. and Schulz, L. (DGM, Oberursel, 1990), p. 1.
4.Quadakkers, W. J., Werkst. Korros. 41, 659 (1990).
5.Korb, G. and Schwaiger, A., High Temp.-High Press. 21, 475 (1989).
6.Moroni, A., Caja, V. L., Sabato, C., Egger, E. L., Gottsauner-Wolf, F., and Chao, E. Y. S., J. Mater. Sci-Mater. M. 5, 411 (1994).
7.Tranquilli, P. Leali, Merolli, A., Palmacci, O., Gabbi, C., Cacchioli, A., and Gonizzi, G., J. Mater. Sci-Mater. M. 5, 345 (1994).
8.Escudero, M. L., González-Carrasco, J. L., García-Alonso, C., and Ramírez, E., Biomater. 16, 735 (1995).
9.Escudero, M. L., López, M. F., Ruiz, J., García-Alonso, M. C., and Canahua, H., J. Biomed. Mater. Res. 31, 313 (1996).
10.Chao, J., González-Carrasco, J. L., Ibáñez, J., Escudero, M. L., and González-Doncel, G., Metall. Mater. Trans. A 27, 3809 (1996).
11.Escudero, M. L. and González-Carrasco, J. L., Biomater. 15, 1175 (1994).
12.López, M. F., Gutiérrez, A., García-Alonso, M. C., and Escudero, M. L., Solid State Commun. 101, 575 (1997).
13.Quadakkers, W. J., Schmidt, K., Grübmeier, H., and Wallura, E., Mater. High Temp. 10, 23 (1992).
14.Versaci, R. A., Clemens, D., Quadakkers, W. J., and Hussey, R., Solid State Ionics 59, 235 (1993).
15.Guttmann, V., Mediavilla, A., and Ruano, O., Mater. High Temp. 11, 42 (1993).
16.Przybylski, K., Garratt-Reed, A. J., Pint, B. A., Katz, E. P., and Yurek, G. J., J. Electrochem. Soc. 134, 3207 (1987).

Related content

Powered by UNSILO

Surface analysis of a heat-treated, Al-containing, iron-based superalloy

  • M. F. López (a1), A. Gutiéerrez (a1), M. C. García-Alonso (a1) and M. L. Escudero (a1)

Metrics

Full text views

Total number of HTML views: 0
Total number of PDF views: 0 *
Loading metrics...

Abstract views

Total abstract views: 0 *
Loading metrics...

* Views captured on Cambridge Core between <date>. This data will be updated every 24 hours.

Usage data cannot currently be displayed.