Phase diagram studies in the quasi binary systems LaMnO3–SrMnO3 and LaMnO3–CaMnO3

  • Peter Majewski (a1), Lars Epple (a1), Michael Rozumek (a1), Heike Schluckwerder (a1) and Fritz Aldinger (a1)...

Abstract

The quasi binary systems LaMnO3–SrMnO3 and LaMnO3–CaMnO3 were studied. Both systems show a miscibility gap at intermediate La:Sr and La:Ca ratios below about 1400 °C in air. This phenomenon causes the decomposition of single-phase (La,Sr)MnO3−x and (La,Ca)MnO3−x solid solution into La-rich SrMnO3−x + Sr-rich LaMnO3−x and La-rich CaMnO3−x + Ca-rich LaMnO3−x at lower temperatures, respectively. At 1400 °C in the system LaMnO3–SrMnO3, a structure transformation of (La,Sr)MnO3 from orthorhombic to rhombohedral with increasing Sr content was not observed, and the structure of La0.7Sr0.3MnO3 was determined to be orthorhombic with a = 0.54927 ± 0.0009 nm, b = 0.54582 ± 0.0009 nm, and c 4 0.76772 ± 0.0034 nm.

Copyright

References

Hide All
1.Rao, C.N.R, Cheetham, A.K., and Mahesh, R., Chem. Mater. 8, 2421 (1996).
2.Proceedings of the Third International Symposium on Solid Oxide Fuel Cells, edited by Singhal, S.C. and Iwahara, H. (The Electrochemical Society, Pennington, NJ, 1993).
3.Urushibara, A., Moritomo, Y., Arima, T., Asamitsu, A., Kido, G., and Tokura, Y., Phys. Rev. B 51, 14103 (1995).
4.van Roosmalen, J.A.M., van Vlaanderen, P., Cordfunke, E.H.P, Ijdo, W.L., and Ijdo, D.J.W, J. Solid State Chem. 114, 516 (1995).
5.Negas, T., J. Solid State Chem. 7, 85 (1973).
6.Horowitz, H.S. and Longo, J.M., Mater. Res. Bull. 13, 1359 (1978).
7.Mitchell, J.F., Argyriou, D.N., Potter, C.D., Hinks, D.G., Jorgensen, J.D., and Bader, S.D., Phys. Rev. B 54, 6172 (1996).
8.Mahendrian, R., Mahesh, R., Rangavittal, N., Tewari, S.K., Raychaudhuri, A.K., Ramakrishnan, T.V., and Rao, C.N.R, Phys. Rev. B 53, 3348 (1995).
9.Kaduk, J. and Wong-Ng, W., Powder Diffraction File, Card No. 49–0416, International Center for Diffraction Data (1993).
10.Grier, D. and McCarthy, G., Powder Diffraction File, Card No. 46–0513, International Center for Diffraction Data (1993).
11.Negas, T. and Roth, R.S., J. Solid State Chem. 1, 409 (1970).
12.MacChesney, J.B., Williams, H.J., Potter, J.F., and Sherwood, R.C., Phys. Rev. 164, 779 (1967).
13.Poeppelmeier, K.R., Leonowicz, M.E., and Longo, J.M., J. Solid State Chem. 44, 89 (1982).
14.Schiffer, P., Ramirez, A.P., Bao, W., and Cheong, S.W., Phys. Rev. Lett. B 53, 3336 (1996).
15.Jain, S.R., Adiga, K.C., and Pai Verneker, V.R., Combust. Flame 40, 71 (1981).
16.Periodic Table on the Elements (VCH, Weinheim, Germany, 1993).

Metrics

Full text views

Total number of HTML views: 0
Total number of PDF views: 0 *
Loading metrics...

Abstract views

Total abstract views: 0 *
Loading metrics...

* Views captured on Cambridge Core between <date>. This data will be updated every 24 hours.

Usage data cannot currently be displayed