Improving the wear resistance of Al–Si alloy by ion implantation

Published online by Cambridge University Press:  31 January 2011

Y. Itoh
Affiliation:
Toyota Central R&D Labs, Inc., 41–1, Aza Yokomichi, Oaza Nagakute, Nagakute-cho, Aichi-gun, Aichi-ken, 480–11, Japan
H. Azuma
Affiliation:
Toyota Central R&D Labs, Inc., 41–1, Aza Yokomichi, Oaza Nagakute, Nagakute-cho, Aichi-gun, Aichi-ken, 480–11, Japan
A. Itoh
Affiliation:
Toyota Central R&D Labs, Inc., 41–1, Aza Yokomichi, Oaza Nagakute, Nagakute-cho, Aichi-gun, Aichi-ken, 480–11, Japan
T. Hioki
Affiliation:
Toyota Central R&D Labs, Inc., 41–1, Aza Yokomichi, Oaza Nagakute, Nagakute-cho, Aichi-gun, Aichi-ken, 480–11, Japan
Get access

Abstract

The mechanical properties of ion-implanted Al–Si alloy were studied using disk samples of alloy irradiated with Ar+, B+, and N2+ ions. Knoop hardness of ASTM 336.0 disks increased from 117 to 165 kgf/mm2 upon N2+ ion implantation. To measure tribological properties, lubricated ball-on-disk tests were performed using steel balls. The coefficients of friction of ion-implanted disks were higher than those of unimplanted ones. Ion implantation improved the wear resistance of the disks, and in the case of N2+ ion-implanted disks, the worn volume was smaller than 10−4 mm3. XPS analysis for the N2+ ion-implanted samples revealed the formation of aluminum and silicon nitride on the sample surface. On the other hand, the cross-sectional image of the ion-implanted surface showed precipitated Si which is held under the implanted N2+ ions.

Type
Articles
Copyright
Copyright © Materials Research Society 1997

Access options

Get access to the full version of this content by using one of the access options below. (Log in options will check for institutional or personal access. Content may require purchase if you do not have access.)

References

REFERENCES

1.McHargue, C. J., Int. Met. Rev. 31, 49 (1986).CrossRefGoogle Scholar
2.Sioshansi, P., Nucl. Instrum. Methods Phys. Res. Sect. B 37/38, 667 (1989).CrossRefGoogle Scholar
3.Partyka, R. J. and Deuchman, A. H., Tech. Pap. Manuf. Eng., TE–87–341 (1987).Google Scholar
4.Williams, J. M., U.S. DOE Rep., CONF–8709117–1–DRAFT (1987).Google Scholar
5.Elder, J. E., Thamburaj, R., and Patnaik, P. C., Int. Mater. Rev. 33, 289 (1988).CrossRefGoogle Scholar
6.Pichat, A., Rabble, L. M., Rieu, J., Rambert, A., Chabrol, C., and Robelet, M., Surf. Coat. Technol. 45, 15 (1991).CrossRefGoogle Scholar
7.Goltsev, V. P., Khodasevich, V. V., Choi, G. H., and Uglov, V. V., Nucl. Instrum. Methods Phys. Res. Sect. B 59/60, 930 (1991).CrossRefGoogle Scholar
8.Jonsson, B. and Hogmark, S., Thin Solid Films 51, 257 (1984).CrossRefGoogle Scholar