Evaluation of Macro- and Micro-Residual Stresses on Textdeed Materials by X-ray, Neutron Diffraction and Defection Measurements

Published online by Cambridge University Press:  06 March 2019

Viktor M. Hauk
Viktor M. Hauk*
Affiliation:
Institut für Werkstoffkunde, Rheinisch Westfälische Technische Hochschule, D-5100 Aachen, F. R, Germany
Get access

Abstract

To evaluate the state of macro- and micro-residual stresses in cold rolled materials of 0.2 to 3 mm thickness the following test methods were used: Measurements of lattice spacing in different directions (φ,Ѱ)with X-rays and neutron-rays on many diffraction peaks. The X-ray method was employed on the surface of the sheet and of the thinned piece after removing several layers from both sides. The neutron-ray method allows measurements in the interior of a specimen and the average of the strain distribution of the total cross section. The etching deflection method determines the macro-residual stresses. The calculation of the macro- anci micro-residual stresses using X-ray elastic constants (XEC) for polycrystalline material and the compliances of single crystals for groups of grains are described. Homogeneous and heterogeneous materials like steels, (α + β)-brass, nickel and copper with 3 % silver were investigated. The state of residual stresses on the surface and with the depth over the cross section was evaluated or is in the final process of investigation.

Type
Research Article
Information
Advances in X-Ray Analysis , Volume 29: Thirty-Fourth Annual Conference on Applications of X-ray Analysis, August 5-9, 1985 , 1985 , pp. 1 - 15
Copyright
Copyright © International Centre for Diffraction Data 1985

Access options

Get access to the full version of this content by using one of the access options below. (Log in options will check for institutional or personal access. Content may require purchase if you do not have access.)

References

1. Dölie, H. and Hauk, V., System of possible lattice strain distributions on mechanically loaded metallic materials (in German) Z. Metallkde. 68: 725 (1977).Google Scholar
2. Hauk, V., Residual stresses. Their importance in science and technology (in German), Conference April 1983, in: “Eigenspannungen, Entstehung - Messung - Bewertung”, Edited by Macherauch, E. and Hauk, V., DGW. beruesel, vol. 1: 9 (1983).Google Scholar
Hauk, V., Stress evaluation on materials having non-linear lattice strain distributions. Adv. X-Ray Anal. 27: 101 (1984).Google Scholar
3. Evensohor, P.D. and Hauk, V., On non-linear distributions of lattice interplanar spacing at X-ray strain measurements (in German), Z. Metallkde. 66: 167 (1975).Google Scholar
Dölie, H.and Hauk, V., Evaluation of residual stress systems arbitrarily oriented by X-rays (in German), HTM. 1: 165 (1976).Google Scholar
4. Dölie, H. and Hauk, V., The theoretical influence of multiaxial depthdependent residual stresses upon the stress measurement by X-rays (in German), HTM. 4: 272 (1979).Google Scholar
5. Hauk, V. and Krug, W.K., The theoretical influence of depth-dependent States of residual stresses upon the stress evaluation by X-rays II. in German), HTM. 9: 273 (1984).Google Scholar
6. Krause, H. and Mathias, M.,An automatic measuring equipment for texture- and stress-analysis by X-rays (in German), HTM. 8: 129 (1983).Google Scholar
7. Wagner, C.N.J. and Boldrick, N.S., The psi-differential and integral methods for residual stress measurements by X-ray diffraction, presented 32. Denver X-Ray Conference (1983).Google Scholar
8. Hoffmann, J., Neff, H., Scholtes, B. and Macherauch, E., Plane polefigures and lattice strain polefigures of textured materials (in German), HTM. 8: 180 (1983).Google Scholar
9. Hauk, V., X-ray methods for measuring residual stress, in “Residual stress and stress relaxation”, Edited by Kula, E. and Weiss, V., Plenum Press New York and London: 117 (1982).Google Scholar
10. Hauk, V. and Vaessen, G., Evaluation of residual stresses by X-rays on textured steels (in German), in: “Eigenspannungen, Entstehung - Messung - Bewertung”, Edited by Macherauch, E. and Bauk, V., DGM. berursel, vol. 2: 9 (1983).Google Scholar
11. Evenschor, P.D. and Hauk, V., X-ray elastic constants and distributions - of icterplanar spacings of materials with preferred orientation (in German), Z. Metallkde. 66: 164 (1975).Google Scholar
12. Hauk, V.. and Sesemann, H., Deviations from linear distributions of lattice interplanar spacings in cubic metals and their relation, to stress measurement by X-rays (in German), Z. Metallkde. 67: 646 (1976).Google Scholar
13. Hauk, V. and Vaessen, G., Evaluation of non-linear lattice strain distribution (in German), in: “Eigenspannungen und Lastspannungen, Moderns Ermittlung - Ergebnisse - Bewertung”, Edited by Hauk, V. and Macherauch, E., HTM-Beiheft, Carl Hanser Verlag München Wien: 38 (1982).Google Scholar
14. Hauk, V.M., Oudelhoven, R.W.M. and Vaessen, G.J.H., The state of residual stress in the near surface region of homogeneous and heterogeneous materials after grinding, Metallurgical Transactions 13A: 1239 (1982).Google Scholar
15. Hauk, V.M. and Vaessen, G.J.H., Residual stress evaluation with X-rays in steels having preferred orientation, Metallurgical Transactions 15 1407 (1984).Google Scholar
16. Noyan, I.C., Equilibrium conditions for the average stresses measured by X-rays, Metallurgical Transactions 14 A: 1907 (1983).Google Scholar
17. Hauk, V. and Stuitje, P.J.T., Phase specific investigations of residual stresses in heterogeneous materials by X-rays after plastic deformations, part I. nd II. in German), Z. Metallkde. 76: 445 and 471 (1985).Google Scholar
18. Bollenrath, F., Hauk, V. and Müller, E.H., Calculation of the elasticity constants of polycrystalline materials from the compliances of single crystals (in German), Z. Metallkde, 58: 76 (1967).Google Scholar
19. Hauk, V.M. and Macherauch, E., A. seful guide for X-ray stress evaluation( XSE), Adv. X-Ray Anal. 27; 81 (1984).Google Scholar
20. Hauk, V., Nikolin, H.J. and Weisshaupt, H., X-ray elasticity constants of a low alloyed steel in two states (in German), Z. Metallkde. 76: 226 (1985).Google Scholar
21. Hauk, V. and Kockelmann, H., Calculation of stress distribution and of XEC. f two-phase-materials (in G.), Z. Metallkde. 68: 719 (1977).Google Scholar
22. Möller, H. and Martin, G., Elastic anisotropy and stress measurement by X-rays (in German), Mitt. Eisenforsch, K.W.I.. Düsseldorf 21: 261 (1939).Google Scholar
23. Willemse, P.F., Naughton, B.P. and Verbraak, C.A., X-ray residual stress measurements on cold-drawn steel wire. Mat. Science Engg. 56: 25 (1982).Google Scholar
24. Hauk, V. and Vaessen, G., Residual stresses in groups of crystallites of steels having preferred orientation [in German), Z. Metallkde, 76: 102 (1985).Google Scholar
25. Hauk, V., Vaessen, G. and Weber, B., The evaluation of residual stresses with rolling-texture (in German), HTM. 0: 122 (1985).Google Scholar
26. Hauk, V., Residual stresses by deformation (in German), in; “Eigenspannungen unc Lastspannungen, Moderns Ermittlung - Ergebnisse - Bewertung”, Edited by Hauk, V. and Macherauch, E., HTM. Beiheft, Carl Hanser Verlag München Wien: 92 (1982).Google Scholar
27. Pintschovius, h., Hauk, V. and Krug, W.K., to be published.Google Scholar
28. Feja, K., Hauk, V. Krug, w.K. and Pintschovius, L., to be published.Google Scholar
29. Hauk, V., Stuitje, P.J.T. and Troost, A., Analysis of the state of residual stresses in a rolled sheet of Cu Zn 40 (in German), Materialprüfung 27: (1985).Google Scholar
30. Hauk, V. and Oudelhoven, H.W.M., to be published.Google Scholar
31. Hauk, V. and Weber, B., to be published.Google Scholar
32. Hauk, V. and Kockelmann, H., Lattice strain distributions of plastically deformed specimens of pure and silveralloyed copper (in German), Z. Metallkde. 71: 303 (1980).Google Scholar